Crosslinking kinetics of polyethylene detected by rheological measurements

中文标题:  
关 键 字: polyethylene  rheology  crosslinking kinetics 
资料类型:  PDF文档
资料大小:  
资料来源:  第十二届全国流变学学术会议
上传时间:  2015-07-22 15:19:00
内容分类  聚合物熔体
资料简介:  Crosslinking kinetics of high density polyethylene (HDPE) with 2,5-di(t-butylperoxy)-2,5-dimethyl-3-hexane(DPDH) ranging from 0.1-1.0wt% was investigated by rheological measurements. Results indicate that a critical gel can be formed at the peroxide concentration of 0.2wt%,below which peroxide decomposition results predominantly long chain branching (LCB) formation. At peroxide concentration above 0.2wt%, however, crosslinking network can be expected. With the increasing of curing temperature, the crosslinking rate at the earlier stage accelerates while the equilibrium modulus at the fully cured stage is independent on temperature. Crosslinking kinetics up to the critical gelpoint at lower curing temperatures of 180 and 190oC can be fitted well by Ding-Leonov’s model.
下载次数: 790次
消耗积分: 2分
 
您还没有登陆
**下载后对该资源进行评论,即可获得2个积分。
本栏目部分资源来自互联网,仅为促进数据共享和信息交流,如有版权问题请告知本网或上传者本人,本网会及时给予答复。
共有0条相关评论 更多>>
请您注意:
·尊重网上道德,遵守中华人民共和国的各项有关法律法规
·承担一切因您的行为而直接或间接导致的民事或刑事法律责任
·本网任何评论,管理人员都有权保留或删除其中的任意内容
·您在本网发表的任何评论,本网有权在网站内转载或引用
·参与本评论即表明您已经阅读并接受上述条款

你还没有登录,无法发表评论

  

互联网站: 中国聚合物网    中国化学仪器网    中国塑料技术网    化学化工论坛
- 网站导航 - 关于我们 - 法律声明 - 广告服务 - 联系我们 -
中国化学会和中国力学会流变学专业委员会(中国流变学会)唯一合作网站
Rheology.cn Copyright(C)2006,All Rights Reserved.
版权所有,未经书面授权,所有页面内容不得以任何形式进行复制